1mm - 25.4mm Solid Pure Aluminum Balls 6060 Aluminum Ball For Special Bearings
Applications |
---|
Special bearings and valves, they are used in automotive industry
(safety devices), shipbuilding industry, aviation and aerospace
industry, electronic industry, welding processes. |
Type | %Si | %Fe | %Mn | %Cr | %Cu | %Al | %Mg | %Zn | %Ti | - | - |
---|---|---|---|---|---|---|---|---|---|---|---|
6061 | 0.40-0.80 | 0.70 max | 0.15 max | 0.04-0.35 | 0.15-0.40 | balance | 0.80-1.20 | 0.25 max | 0.15 max | - | - |
Series | Description | Available heat treatments |
---|---|---|
6xxx | Al-Si-Mg alloy | 6061 T6 |
Property | Symbol | U.o.M. | Type | Notes | Values |
---|---|---|---|---|---|
Density | δ | [g/cm3] | Physical | Room temp. | 2.70 |
Young's modulus | E | [GPa] | Mechanical | - | 69 |
Specific heat | c | [J/kg-K] | Thermal | Room temp. | 898 |
Coefficient of linear thermal expansion | α | [10^-6/ºC] | Thermal | (ΔT=0-100°C) | 23.8 |
Thermal conductivity | λ | [W/(m·K)] | Thermal | Room temp. | 168.0 |
Electric resistivity | ρ | [Ω*m*10^-9] | Electric | - | 40 |
Relative magnetic permeability | µ | - | Magnetic | Paramagnetic | 1.004 |
Property | Type | U.o.M. | Values | U.o.M. | Values |
---|---|---|---|---|---|
Hardness | Mechanical | [HV0.5] | 85 - 105 | - | - |
Ultimate tensile strength | Mechanical | [MPa] | 280 - 340 | [psix10^3] | 41 - 49 |
Service temperature | Thermal | [ºC] | -196 / 200 | [ºF] | -320.8 / 392 |
Diameters (min/max) | U.o.M. | Diameters (min/max) | U.o.M. | Precision grades (ISO 3290 / AFBMA) |
---|---|---|---|---|
1.000 - 150.000 | [mm] | 3/64 - 6 | ["] | G100-200-500-1000 |
Corrosion Resistance |
---|
Good corrosion resistance in atmosphere and water, even in marine
environment. Corrosion resistance of 6xxx series alloy is usually
slighlty lower than 1xxx and 5xxx series. Intergranular corrosion
in aggressive environments due to the allowed copper content can be
reduced by means of suitable heat treatments. They are subjected to
pitting corrosion in presence of chlorides. |